Interfacial fracture mechanism associated with mixed oxides growth in thermal barrier coating system
发布时间：2025-04-30
点击次数：
- 发布时间：
- 2025-04-30
- 论文名称：
- Interfacial fracture mechanism associated with mixed oxides growth in thermal barrier coating system
- 发表刊物：
- Surface and Coatings Technology
- 摘要：
- Abstract The interfacial failure mechanism of the thermal barrier coating system (TBCs) was
numerically investigated by considering the role of mixed oxides (MO), which was induced
by the discontinuous α-Al 2 O 3 at the interface between top and bond coatings. It is shown
that MO has a significant effect on the interface integrity. High growth rate of MO will induce
the initiation and propagation of interface cracks and eventually results in the debonding of
ceramic coating. The high coverage ratio of MO at the interface will accelerate the ...