A study of fatigue damage evolution on pulsed Nd YAG Ti6Al4V laser welded joints
Release Time:2025-04-30
Hits:
- Date:
- 2025-04-30
- Title of Paper:
- A study of fatigue damage evolution on pulsed Nd YAG Ti6Al4V laser welded joints
- Journal:
- Engineering Fracture Mechanics
- Summary:
- The influence of the large microstructure gradient the fatigue damage behaviour of laser beam welded Ti6Al4V was investigated. The experimental results showed that the damage evolution of fatigue residual strength in the LBW joint was higher than that in the base metal (BM) sample, and the fatigue crack growth resistance of the fusion zone (FZ) in the LBW joint was greater than that of the BM. Compared with BM specimens, the heterogeneous micro-plastic deformation was easier to obtain in the LBW joint under fatigue load due to high large microstructure gradient, which promotes crack initiation in the LBW welded joint.
- Co-author:
- J Liu, XL Gao , LJ Zhang* , JX Zhang
- Volume:
- 117
- Page Number:
- 84–93
- Translation or Not:
- No
- Date of Publication:
- 2014-01-15
- Prev One:Nd YAG激光器焊接钛合金薄板的工艺研究
- Next One:SiC_p/ZL101铝基复合材料的原位强化活性液相扩散焊方法(In situ A-TLP)