Corrosion protection and failure mechanism of ZrO2 coating on zirconium alloy Zry-4 under varied LiOH concentrations in lithiated water at 360 °C/18.5 Mpa

发布时间：2025-04-30 点击次数：

发布时间：2025-04-30

论文名称：Corrosion protection and failure mechanism of ZrO2 coating on zirconium alloy Zry-4 under varied LiOH concentrations in lithiated water at 360 °C/18.5 Mpa

发表刊物：Applied Surface Science

合写作者：Guanyu Jiang, Donghai Xu*, Junhao Liu, Jianqiao Yang, Yanhui Li, Wenjun Kuang

是否译文：否

发表时间：2024-03-30