Insights into oxidation and nitridation of alumina-forming FeCrAl alloy after supercritical water exposure: Effect of pre-corrosion on high-temperature damage behavior

发布时间：2025-04-30 点击次数：

发布时间：2025-04-30

论文名称：Insights into oxidation and nitridation of alumina-forming FeCrAl alloy after supercritical water exposure: Effect of pre-corrosion on high-temperature damage behavior

发表刊物：The Journal of Supercritical Fluids

合写作者：Guanyu Jiang, Donghai Xu*, Huanteng Liu, Bing He, Lu Liu, Yanhui Li, Jianqiao Yang