Additive manufacturing of ZrO2 ceramic dental bridges by stereolithography
发布时间：2025-04-30
点击次数：
- 发布时间：
- 2025-04-30
- 论文名称：
- Additive manufacturing of ZrO2 ceramic dental bridges by stereolithography
- 发表刊物：
- Rapid Prototyping Journal
- 摘要：
- Purpose–This paper aims to develop an additive manufacturing technique for complex zirconia ceramic dental bridges.
Design/methodology/approach–To carry out this study, a dental bridge model was obtained by three dimensional reverse engineering and a light-curable zirconia ceramic suspension was formulated. Zirconia bridges were manufactured by stereolithography, and then treated by vacuum freeze drying, vacuum infiltration and sintering. The optimal scanning speed was determined according to the shape precision comparison. Then, characteristics of the sintered ceramic parts were tested as size shrinkage, relative density, surface Vickers hardness, surface roughness, and microstructure.
Findings–The method for preparation of light curable zirconia suspension (40vol%solid loading) with a viscosity value of 127mPa•s was proposed. The optimal laser scanning speed for zirconia bridge fabrication was 1200 mm/s. A relative density of 98.58% was achieved; the obtained surface Vickers hardness and surface roughness were 1398 HV and 2.06 μm, respectively.
Originality/value–This paper provides a potential technical method for manufacturing complex zirconia dental bridges and other small complex-shaped ceramic components which are difficult to be made by other manufacturing techniques.
Authors: Q Lian, WQ Sui, XQ Wu, F Yang, SP Yang
- 合写作者：
- Q Lian*, WQ Sui, XQ Wu, et al.
- 是否译文：
- 否
- 发表时间：
- 2017-02-25