- Tilting separation analysis of bottom-up mask projection stereolithography based on cohesive zone model
- 发表刊物：
- Journal of Materials Processing Technology
- 摘要：
- Compared with top-down stereolithography, bottom-up mask projection stereolithography can reduce the start filling volume of vat and is able to build components with high-viscosity materials. For general photosensitive materials, a separation process is required to separate the cured layer from the resin vat surface in order to accomplish the fabrication of current layer. The separation process can be achieved without damaging the part by utilizing appropriate platform motions including pulling-up, tilting and shearing, and covering inert film on the vat surface. The tilting separation is used in both industrial and academic area, however lack of study compared with pulling-up separation. The mechanism of tilting separation and its effects on separation force and fabrication process are not clear. In this paper, an analytical model based on cohesive zone model was formed and a specialized test system was built. Experimental research that studied the tilting effects on cohesive stiffness and fracture energy was conducted by collecting and analyzing separation force data. The results showed that changing exposure area function or the part fabrication orientation could change the cohesive stiffness, and increasing tilting separation speed could cause different increase in fracture energy when using different inert films. The results of this investigation can be used to choose the reasonable platform motion and process parameters by considering the part geometry and the characteristics of both inert film and materials.
- 合写作者：
- XQ Wu, Q Lian*, DC Li, ZM Jin
- 是否译文：
- 否
- 发表时间：
- 2016-12-20