Influence of sulfidation treatment on the structure and tribological properties of nitrogen-doped diamond-like carbon films
发布时间：2025-04-30
点击次数：
- 发布时间：
- 2025-04-30
- 论文名称：
- Influence of sulfidation treatment on the structure and tribological properties of nitrogen-doped diamond-like carbon films
- 发表刊物：
- Applied Surface Science
- 摘要：
- The nitrogen-doped diamond-like carbon (DLC) films were deposited on high speed steel (HSS) substrates in the direct current unbalanced magnetron sputtering system. Sulphurized layer was formed on the surface of DLC films by means of liquid sulfidation in the intermixture of urea and thiourea solution in order to improve the tribological properties of DLC films. The influence of sulfidation treatment on the structure and tribological properties of DLC films was investigated in this work. The structure and wear surface morphology of DLC films were analyzed by Raman spectroscopy, XPS and SEM, respectively. It reveals that the treated films are smooth and uniform; and sulfur atoms are bonded chemically. The treated films have broader distribution of Raman spectra in the range of 1000–1800 cm−1 and higher ID/IG ratio than the untreated films as a result of the appearance of the crystalline graphite structure after the sulfidation treatment. It is showed that the sp2 relative content increase in the treated films from the XPS measurement. The Raman results are consistent with the XPS results. The tribological properties of DLC films were investigated using a ball-on-disk rotating friction and wear tester under dry friction conditions. It is found that the sulfidation concentration plays an important part in the tribological properties of the treated DLC films. The results showed the treated films with low sulfidation concentration have a lower friction coefficient (0.1) than the treated films with high sulfidation concentration (0.26) and the untreated films (0.27) under the same friction testing conditions, which can be attributed to both the presence of sulfur-containing materials and the forming of the mechanical alloyed layer on the wear surface. Adding the dry nitrogen to the sliding surface in the testing system helps the friction coefficient of the treated films with low sulfidation concentration to decrease to 0.04 further in this work. On the basis of the experimental results, it is indicated that the liquid sulfidation technique, which is low-cost, non-polluting and convenience, would be an appropriate method for the surface treatment of DLC films.
- 合写作者：
- Guang-Neng Dong，el
- 是否译文：
- 否
- 发表时间：
- 2007-12-01