- Cryogenic dielectric and mechanical properties of Nanowire-Al2O3 filled PBT/GF composites
- 发表刊物：
- 2006 1ST IEEE INTERNATIONAL CONFERENCE ON NANO/MICRO ENGINEERED AND MOLECULAR SY
- 摘要：
- The cryogenic dielectric and mechanical properties of nanowire-Al2O3 filled PBT/GF (glass fiber) composites are investigated by combing macro-performances testing and microstructures analysis. Compared with PBT/GF composites, the PBT/GF/Al2O3 ternary systems present improved tensile strength as well as impact strength. The fracture surface shows a typical toughened characteristic under SEM observation, which may be explained by the 'crack bridging' toughening mechanism. At the same time, POM study indicates diminished spherulitic texture for the three phase composites, which is due to nucleating effect of the nanoparticles. DSC and WAXD analysis suggest that nanowire-Al2O3 can hinder the crystal growth and lower the degree of crystallinity. Cryogenic dielectric spectra of the composites showed a broad gamma loss process shifting to low temperature region with the increasing content of Al2O3, Which suggested that the existence of the nanowire might facilitate the molecular motions of PBT matrix and improved the low temperature toughness. Suitable amount of Al2O3 can also be helpful to reduce the micro-defects, which may contribute to the higher electrical strength of the systems.
- 合写作者：
- Yu, Demei; Xie, Yunchuan; Wan, Weitao;
- 是否译文：
- 否
- 发表时间：
- 2006-01-01