Preparation of La3+, carbon nanotube doped nanometer TiO2 with sol-gel method and photocatalytic activity of doped nanometer TiO2
发布时间：2025-04-30
点击次数：
- 发布时间：
- 2025-04-30
- 论文名称：
- Preparation of La3+, carbon nanotube doped nanometer TiO2 with sol-gel method and photocatalytic activity of doped nanometer TiO2
- 发表刊物：
- Journal of Xi'an Jiaotong University
- 摘要：
- Three kinds of doped TiO2 particles, include La3+ doped, multi-wall carbon nanotube (MWCNT) doped and their co-doped TiO2, were prepared by sol-gel method. The catalytic activity of doped TiO2 was evaluated via ultraviolet light degradation experiments of methyl orange. It is found that La3+ doped TiO2 particles demonstrates a higher photocatalytic activity than that of pure TiO2, and an optimum value is reached at doped concentration of 0. 08% (mole fraction). CNT doped TiO2 can also improve the photocatalytic activity of TiO2. Besides, TiO2 particles co- doped with La3+ and CNT show the highest photocatalytic activity. As for co-doped TiO2, the decomposition ratio of methyl orange solution reaches 84% in 1 h, while it gets 53% for pure TiO2. The microstructure of the particles is characterized with XRD and TEM techniques. These particles are endowed with anatase crystal phase of about 8-25 nm diameter.
- 合写作者：
- Guo Xiusheng; Yu Demei; Zhang Ning; Bofeng, W.; Qiao Chunmiao; Xie Yunchuan; Wan
- 是否译文：
- 否
- 发表时间：
- 2008-10-01