A graphite nanoplatelet/epoxy composite with high dielectric constant and high thermal conductivity
发布时间：2025-04-30
点击次数：
- 发布时间：
- 2025-04-30
- 论文名称：
- A graphite nanoplatelet/epoxy composite with high dielectric constant and high thermal conductivity
- 发表刊物：
- CARBON
- 摘要：
- A simple strategy for the preparation of composites with high dielectric constant and thermal conductivity was developed through a typical interface design. Graphite nanoplatelets (GNPs) with a thickness of 20-50 nm are fabricated and homogeneously dispersed in the epoxy matrix. A high dielectric constant of more than 230 and a high thermal conductivity of 0.54 W/mK (a 157% increase over that of pure epoxy) could be obtained for the composites with a lower filler content of 1.892 vol.%. The dielectric constant still remains at more than 100 even in the frequency range of 10(5)-10(6) Hz. When loaded at 2.703 vol.%, GNP/epoxy composites have a dielectric constant higher than 140 in the frequency range of 10(2)-10(4) Hz and a high thermal conductivity of 0.72 W/mK, which is a 240% increase over that of pure epoxy. The high dielectric constant and low loss tangent are observed in the composite with the GNPs content of 0.949 vol.% around 10(5)-10(6) Hz. It is believed that high aspect ratio of GNPs and oxygen functional groups on their basal planes are critical issues of the constitution of a special interface region between the GNPs and epoxy matrix and the high performance of the composites.
- 合写作者：
- Min, Chao; Yu, Demei; Cao, Jingyu; Wang, Guolong; Feng, Lihua
- 是否译文：
- 否
- 发表时间：
- 2013-03-01