- Rapid pyrolysis and CO2 gasification of anthracite at high temperature
- 发表刊物：
- JOURNAL OF THE ENERGY INSTITUTE
- 摘要：
- Anthracite could be burnt efficiently at high temperature utilizing oxy-coal technology. To clarify the effects of temperature and atmosphere on char porosity characteristics, char morphology, fuel-N conversion, and reducing products release, rapid pyrolysis and CO2 gasification of anthracite was carried out in a high temperature entrained-flow reactor to simulate the condition in a pulverized coal furnace. Developed pore structure was formed in the gasification chars, which could be contributed to char-CO2 reaction at high temperatures. More mesopores were formed in internal carbon skeleton and retained against collapse and coalescent for gasification chars than pyrolysis chars. Compared with pyrolysis char, smoother and denser surface was observed in gasification char with the irregular bulges disappeared due to the destruction of external carbon skeleton. Char-N could be oxidized to NO in CO2 atmosphere and then reduced to N-2 by (-CN) on the char surface. Char-N release was greatly promoted due to gasification reaction along with poly-condensation at high temperature; and the preact release of char-N would result in a larger portion of NOx reduction in the following reduction zone with the oxygen-staging combustion technology compared with that in air-staging combustion. Complementally, homogeneous reduction in NOx emission would play a minor effect for anthracite in oxy-coal combustion because of the deficiency of CH4 and HCN, especially at high temperature. (C) 2017 Energy Institute. Published by Elsevier Ltd. All rights reserved.
- 合写作者：
- Zha, Qiongliang ; Zhao, Jing ; Wang, Chang'an ; Che, Defu
- 是否译文：
- 否
- 发表时间：
- 2018-12-12